How To Straigten Small Brass Tubing?

countryguy

countryguy

Active User
Registered
Joined
May 7, 2014
Messages
776
Hi all. Is there a trick someone can point out to me to straighten this pipe out? (pic below). Searched and see tube straighteners, but I cannot remove this. So it's Heat it, or some trick I'm clueless about.
TIA!!!


straightenBrassPipe1.jpg
 
I would think annealing it would make it easier to bend.
To prevent kinking, maybe wrap it with some copper wire if you can't get a bending spring on it.
if you can get the tube out of the piece it would make it easier to do it.
 
I'm thinking a little heat might be the best. Just heating the brass anneals it. Brass is hardened by working it.
 
+3 on annealing.
as a suggestion fill the tube with a piece of wire just smaller than the ID of the tube (post anneal).
it will prevent tube collapse
 
Annealing would be appropriate. I think I would take a piece of round stock just shy of the ID, and shape a full radius end on it. Working all hand held, tap lightly and put a little pressure in the "straightening" direction. Use a little grease on the half-ball shape and it should not take much force. Make the end of the rod as smooth as possible. The rod will keep the tubing from collapsing and keep it all round. You shouldn't have to anneal it beyond the initial process. That may not be absolutely necessary, but since the temper is unknown, but we do know that it work hardens from bending, we can safely say it is harder than it originally was and there could be a risk of cracking if it was already at a hard temper. Don't heat it and try to work it while hot.

How straight is "straight" in this instance? How much pressure is on it? It looks like a bit of gas plumbing from a welder. Is that a solenoid operated valve it goes into?
 
Wouldn't it be easier to just cut the old tube, ream it out and sweat in a new, straight tube?
 
GReat stuff folks! Best of both worlds here. 1) I took to you guys first so I did not ruin in. 2) Heated the joint and the thread-lock or whatever melted and I took out the brass pipe from the device itself. I can remove the ground strap and run it into a straighter now or try some heat.

This is an S45 Plasma torch head. It's part of my 2nd 3D printer project to make a new plasma Torch head assy for my machine torch. (now a lonely hollow aluminum tube). The old head was a molded plastic head also. Parts were a cool $180..... Unless you have Fusion360, the H-M forum, and a 3D printer.... Then it's about $45 :) That above needs to fit into this: (pics below) And it's really a close fit. We'll see!

IMG_0428.JPG IMG_0437.JPG
 
Last edited:
When you straighten a bend. The outside radius compresses and the inside radius of the arc/bend stretches. I would ONLY heat up the inside radius of the bend because of this. Heating the outside also, would probably cause a failure in uniformity. Stuffing a rod down the ID doesn’t sound workable. You would never get the rod into the bend area until you got the tube straight, if you got the tube straight. I would make/find a half round shoe/mandrel and work out the bend. Better yet maybe just change out the tube for new and straight. Good Luck, Dave.
 
Whatever you do, take pictures for us! I'd love to see how this works out.
 